Pps /PTFE /Fg blend high temperature felt filter bag

Material TDS as Follows PPS +PTFE Blended FeltPFTE Emulsion SoakingN-(PTFE+PPS+FG)/FG-900G30% Super fine PPS fabric on surface Weight per Square Meter (Normal)900 GMaterial (Fiber/Scrim)(PTFE40%+PPS30%+FG30%)/FGThickness2.8 mmAir permeability24  M3/M2.Min@200PaWarp Tensile Strength> 2500N/5×20cmWeft Tensi

Featured Products

Material TDS as Follows
PPS +PTFE Blended Felt
PFTE Emulsion Soaking
30% Super fine PPS fabric on surface 
Weight per Square Meter (Normal)900 G
Material (Fiber/Scrim)(PTFE40%+PPS30%+FG30%)/FG
Thickness2.8 mm
Air permeability24  M3/M2.Min@200Pa
Warp Tensile Strength> 2500N/5×20cm
Weft Tensile Strength> 2500N/5×20cm
Warp Elongation< 10%/(5×20cm)
Weft Elongation< 15%/(5×20cm)
Continuous service Temperature< 240ºC
Instant (<10Min.) Temperature bears < 260ºC
 Liner Shrinkage@130 ºCMD<0.3%, XD<0.3%
 Mechanical FinishHeat Setting, Calendering
 Chemical Finish/
 Mullen (PSI)/
 Water Repellent/
 Surface Electric-Resistance/
Special Surface or Deep Treatment
(In case client specially request to)
PTFE Membrane Laminated (PTFE-ML),
or PFTE Emulsion Soaking (PTFE-ES)
Other Customise RequestsAcceptable depends on MOQ.

Bag top normally has two types of structures, or customised:
Hight Temperature PPS /PTFE /Fg Blend Felt Filter BagHight Temperature PPS /PTFE /Fg Blend Felt Filter Bag