Material TDS as Follows
Bag top normally has two types of structures, or customised:
| Aramid Felt -ES | N-ARM/PTFE-550G/PTFE-ES PTFE-ES : PFTE Emulsion Soaking |
| Weight per Square Meter (Normal) | 550 G |
| Material (Fiber/Scrim) | ARM/PTFE |
| Thickness | 1.9~2.3 mm |
| Air permeability | 15~20 M3/M2.Min@200Pa |
| Warp Tensile Strength | > 900N/5×20cm |
| Weft Tensile Strength | > 1300N/5×20cm |
| Warp Elongation | < 30%/(5×20cm) |
| Weft Elongation | < 40%/(5×20cm) |
| Continuous service Temperature | < 204ºC |
| Instant (<10Min.) Temperature bears | < 240ºC |
| Liner Shrinkage@130 ºC | MD<1.5%, XD<1% |
| Mechanical Finish | Heat setting, singeing, calendering PTFE-ES : PFTE Emulsion Soaking |
| Chemical Finish | / |
| Mullen (PSI) | / |
| Water Repellent | / |
| Surface Electric-Resistance | / |
| Special Surface or Deep Treatment (In case client specially request to) | PTFE Membrane Laminated (PTFE-ML), or PFTE Emulsion Soaking (PTFE-ES) |
| Other Customise Requests | Acceptable depends on MOQ. |